Technical Information Audental Ultra SLM Powder
PRODUCT NAME:Audental Ultra
DESCRIPTION: Cobalt based dental laser sintering alloy, type 5
GRAIN SIZE: 15 – 45μm
Manufacturer:QHD Audental Advanced Material CO., Ltd.
Address:2F, North D, BD 16, 1 Yanghe Road, Development Area, QHD, China.
Post:066004 Tel:+86-335-8691917
CHEMICAL COMPOSITION:
Co: 64%, Cr: 28 %, Mo: 6%, Si, Mn, Fe<1.0%
TECHNICAL DATA
Yield strength 0.2 %: 550 MPa
Elongation: 7 %
Density: 8.55 g/cm3
Tensile strength: 980 MPa
E-module: 200 GPa
Tarnish resistance: yes
Corrosion resistance :< 200 μg/cm²
Hardness: 320 HV 10
Indication: Crowns and bridges, implant supported superstructures and bars.
Storage conditions: Store in airtight containers and keep dry
Instruction for use Audental Ultra SLM Powder
Intended Use
Audental Ultra is cobalt based alloy intended for production of removable partial dentures restorations in laser sintering machine, Please refer to the operating instructions of the system manufacturer.The powder is class IIa medical device in accordance with annex IX rule 8 of the MDD 93/42/EEC. Composition corresponds to “type 5” CoCr dental material according to ISO 22674.
CAD
Design the upper removable partial denture with a minimum thickness of 0.7 mm. For minor connectors use a diameter of 1.2 x 1.8 mm. For the sublingual bars of a lower partial denture, a diameter of 4 x 2 mm is recommended. Take care of adequate material thickness on clasps.
Thermal treatment
After the laser sintering process, the building boards have to pass heat treatment to minimize stresses due to the laser sintering process. For this purpose,a suitable furnace with inert gas (argon) or vacuum function should be used. Stress relieving without inert gas atmosphere can optionally be performed.Please consider that a treatment without inert gas atmosphere can lead to an increased oxide formation. Heat up to 1000°C with inner gas within 45 mins to keep 30 mins, then take out and let cool down freely in ambient air.
Remove Parts from the build plate
Removal of restorations from platform: After stress relieving and cooling down of the platform, remove the parts from building platform using band saw, rotary cutter or pliers. Remove the remains of the supports using pliers.
Preparation before ceramic veneering
The frameworks can be elaborated with standard carbide cutters, look for smooth transitions and avoid overlapping material. Please use the same cutter for one alloy to avoid contamination. It´s recommended that he frame needs to be sandblasted with aluminium oxide 125µm and 3-4 bar to remove the present oxide layer thoroughly. In the end the cleaning by steam cleaner is mandatory. If you use a ceramic bonder please consider the instruction for use of the manufacturer.
Contraindications and side effects
If the instructions are observed during the production processes, incompatibilities with non-precious dental alloys are extremely rare. In case of a proven allergy against an ingredient of this alloy, the alloy must not be used for safety reasons. In exceptional cases, electrochemically induced, local irritations have been reported. When different alloy groups are used, galvanic effects might occur.
|
|
Audental Ultra SLM Powder/CoCrMo/CE,FDA,IdentAlloy/Dental 3D Metal Print Images
|